What is the purpose of the surface pretreatment of the coating boundary in the coating process?

We all know that nanoparticles have self aggregation effect due to their large surface energy. On a flat surface, a layer of nanoparticles is stacked on the surface. With the rise of temperature, 

Influence of different precursor gases on DLC film

In the process of DLC film preparation, hydrocarbon precursor gases are used, and different precursors have different effects on the performance of the film.

Comparative study on the discharge of HiPIMS with or without local ionization zone

Due to the constraint of magnetic field and the ultra-high power discharge, the high-power pulsed magnetron sputtering technology (HiPIMS) has the unstable phenomenon of glow flicker due to the partial discharge enhancement during the discharge process.

Sio2-ta2o5 optical interference films were prepared by HiPIMS reaction sputtering

When Si target and Ta target oxygen reaction sputtering, the intake hysteresis loop can be inhibited by using appropriate HiPIMS pulse parameters, and the process stability can be ensured even without gas controller.

Corrosion resistance of diamond-like film deposited on inner wall of steel pipe

Effect of DC bias on properties of C: SiOX film prepared by HMDSO

The C: SiOX film prepared by HMDSO has excellent corrosion resistance. The influence of HMDSO/O2 ratio on the composition, corrosion resistance and hardness of the film was discussed in the last part. In the whole coating process, 

HiPIMS self-organizing discharge high-resolution spectral imaging

Due to the constraint of magnetic field and the ultra-high power discharge, the high-power pulsed magnetron sputtering technology (HiPIMS) has the unstable phenomenon of glow flicker due to the partial discharge enhancement during the discharge process.

Sputtering characteristics of HiPIMS reaction